OIM 65% Porcelain ceramic ball is in chemical composition 70+% alpha alumina. Because of its high alumina content and low silica (SiO2 ), it's a very Excellent and ideal product for high temperature and steam applications, such as Secondary reformers in ammonia processing, where leached silica will coat downstream equipment or foul the catalyst bed.OIM alumina support media has very excellent thermal properties, with its high density high-temperature resistance 1450℃, also it's a good choice for heat retention or equilibration media. For its superior chemical resistance, it's suitable for applications in olefin processes, such as ethylene dryers, where there's the polymerization problem.
Type | Inert Alumina Ball-65 | |||||||||||
Color | White gray | |||||||||||
Shape | Ball | |||||||||||
Chemical composition | Min. % | Max. % | Usual % | |||||||||
Al2O3 | 65 | 70 | 68.0 | |||||||||
SiO2 | 20 | 25 | 23.0 | |||||||||
Al2O3 + SiO2 | 90 | 93 | 91 | |||||||||
Fe2O3 | / | 0.3 | 0.02 | |||||||||
TiO2 | / | 0.1 | 0.02 | |||||||||
CaO | / | 4.0 | 1.5 | |||||||||
MgO | / | 0.1 | 0.05 | |||||||||
Na2O | / | 0.25 | 0.1 | |||||||||
K2O | / | 0.2 | 0.13 | |||||||||
Physical properties | Leachable Iron (%) | ≤0.01 | ||||||||||
Apparent Porosity by Weight | ≤7.0 | |||||||||||
H2O absorption (wt.%) | <1.0 | |||||||||||
Acid resistance (%) | >99.8 | |||||||||||
Alkaline resistance (%) | >85 | |||||||||||
Bulk Density | (g/cm3) | 1.35 | ||||||||||
(lb/ft3) | 84 | |||||||||||
Specific density | (kg/m3) | 2300 | ||||||||||
(lb/ft3) | 144 | |||||||||||
Moh’s hardness (scale) | >7.0 | |||||||||||
Thermal conductivity (w/m2.k) | 0.7-0.8 | |||||||||||
Thermal Expansion @ 500 | 0.10% | |||||||||||
Max. Operating Temperature (℃) | 1050 | |||||||||||
Thermal expansion @ 500℃ | 0.1% | |||||||||||
Thermal Shock Stability (times) (500 ℃ then water cooling) |
10 | |||||||||||
Geometric properties | Nominal Size | (mm) | 3 | 6 | 10 | 13 | 16 | 19 | 25 | 38 | 50 | |
(inch) | 1/8 | 1/4 | 3/8 | 1/2 | 5/8 | 3/4 | 1 | 1.5 | 2 | |||
Crush Strength Min. | (lbs) | 84 | 209 | 282 | 616 | 770 | 1738 | 1936 | 2156 | 3564 | ||
(kg) | 459 | 101 | 150 | 347 | 398 | 827 | 908 | 1010 | 1755 | |||
(N/PC) | 450 | 990 | 1470 | 3400 | 3900 | 8100 | 8900 | 9900 | 17200 |
1. High compressive strength;
2. Stability, acid and alkali resistance;
3. Support and protect active catalyst;
4. Sufficient stock of common types balls and timely delivery.